How to Bake Enameled Copper Wire?

As an Enameled Copper Wire Manufacturer, share with you.

After the wire is painted, it enters the oven, first evaporates the solvent in the paint solution, then solidifies to form a layer of paint film, paints and bakes, and repeats this several times to complete the baking process of the enameled bag.

1. Oven temperature distribution

The temperature distribution of the oven has a great relationship with the baking of the enameled wire. The distribution of oven temperature has two requirements: longitudinal temperature and transverse temperature. The longitudinal temperature requirements are curvilinear, that is, from low to high, and then from high to low. The lateral temperature requires a linear shape. The uniformity of the lateral temperature depends on factors such as equipment heating, heat preservation, and hot air convection.

The enameling process requires the enameling furnace to meet

Enameled Copper Wire

Enameled Copper Wire

a) Accurate temperature control, ±5℃

b) The furnace temperature curve can be adjusted, and the maximum temperature of the curing zone can reach 550℃

c) The lateral temperature difference does not exceed 5°C.

There are generally three types of temperatures in the oven: heat source temperature, air temperature, and wire temperature. It is customary to say that the furnace temperature is measured by a thermocouple placed in the air, and the temperature is generally close to the temperature of the gas in the furnace. T source>T gas>T paint>T line (T paint is the temperature at which the paint produces physical and chemical changes in the oven) Generally, T paint is about 100°C lower than T gas.

The longitudinal direction of the oven is divided into an evaporation zone and a solidification zone. The evaporation zone is mainly used for evaporating the solvent, and the curing zone is mainly used for curing the paint film.

Our company also has Enameled Copper Wire on sale, welcome to contact us.